Technical data
- Material
- Polypropylene/polyglycolic acid-caprolactone
- dyed / monofilament / partially absorbable / macroporous
- Absorption profile
- The PGACL portion is absorbed within 90-120 days.
partially in combination with:
- Material
- Polydioxanone
- dyed / monofilament / absorbable
- Absorption profile
- 50% tensile strength after 28 - 42 days
0% tensile strength after 180 - 210 days
Downloads
-
SERATOM® PA delivery programme Version 12/2019
-
Instructions for use SERAMESH®, SERATOM®, SERATIM®, SERASIS®, SERATEX®, SERAGYN® Version 2023-05 – CE090018
Security with system
The products have a bicomponent polypropylene/polyglycolic acid-caprolactone structure.
The use of SERATOM® allows a minimally-invasive, tension-free, surgical concept that can be performed via the vagina. It can be used when findings show traction cystoceles in need of surgical correction, with or without a stable cervix, and also as part of an overall concept for vaginal surgery in cases of incomplete or complete prolapse.
Product range
Icon | Model | Art.No. | PU | |
---|---|---|---|---|
SERATOM® A PA MR, 5x10 cm |
SN205MR | 3 | ||
SERATOM® A PA MR, 5x10 cm |
SN205MR50 | 1 | ||
SERATOM® MN PA MR 3x3 cm |
SN207MR | 3 | ||
SERATOM® MN PA MR 3x3 cm |
SN207MR50 | 1 | ||
SERATOM® MN2 PA MR 3x3 cm |
SN208MR | 3 | ||
SERATOM® MN2 PA MR 3x3 cm |
SN208MR50 | 1 | ||
SERATOM® E PA MR, 6x10 cm |
SN215MR | 3 | ||
SERATOM® E PA MR, 6x10 cm |
SN215MR50 | 1 | ||
SERATOM® E PA MR, 6x10 cm |
SN217MR | 3 | ||
SERATOM® E PA MR, 6x10 cm |
SN218MR | 3 | ||
SERATOM® F PA MR, 5,5x10cm |
SN245MR | 3 | ||
SERATOM® F PA MR, 5,5x10cm |
SN245MR50 | 1 | ||
SERATOM® K PA MR, 7,5x24 cm |
SN285MR | 3 | ||
SERATOM® K PA MR, 7,5x24 cm |
SN285MR50 | 1 | ||
SERATOM® K2 PA MR, 7,5x24 cm |
SN287MR | 3 | ||
SERATOM® L PA MR, 7,5x9cm |
SN295MR | 3 | ||
SERATOM® L PA MR, 7,5x9cm |
SN295MR50 | 1 | ||
SERATOM® P PA MR, 4x9 cm |
SN845MR | 3 | ||
SERATOM® P PA MR, 4x9 cm |
SN845MR50 | 1 | ||
SERATOM® P2 PA MR, 4x25 cm |
SN875MR | 3 | ||
SERATOM® G2 PA MR, 5x23 cm |
SN895MR | 3 |